 note = {This study researched the bending strength of next 2step stage Shigaraki clays, the temporary sintered clay and the sintered clay of which were contained oxidize ceramic powders at a fixed rate. In the previous study, we used Al_2O_3 ceramic powders. But in this study, we used ZrO_2 ceramic powders. As the result, the temporary sintered clay declined the bending strength as we increased content of ZrO_2. On the contrary, when the clay was sintered at 1230℃, the addition rate of ZrO_2 ceramic powders at 25wt% showed maximum the bending strength σ=66.5[MPa However, the increase of the bubble accompanied by the addition rate increase was observed., application},