{"_buckets": {"deposit": "e9c84d1d-4527-4bd3-a0d9-115e344bf95b"}, "_deposit": {"created_by": 1, "id": "23623", "owners": [1], "pid": {"revision_id": 0, "type": "depid", "value": "23623"}, "status": "published"}, "_oai": {"id": "oai:shinshu.repo.nii.ac.jp:00023623", "sets": []}, "author_link": ["95679", "95680"], "item_20003_alternative_title_1": {"attribute_name": "その他(別言語等)のタイトル", "attribute_value_mlt": [{"subitem_alternative_title": "The influence of heat treatment on the fatigue strength of laser-welded titanium"}]}, "item_20003_creator_3": {"attribute_name": "作成者(その他言語)", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "三溝, 恒幸"}], "nameIdentifiers": [{"nameIdentifier": "95679", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Samizo, Tsuneyuki"}], "nameIdentifiers": [{"nameIdentifier": "95680", "nameIdentifierScheme": "WEKO"}]}]}, "item_20003_date_19": {"attribute_name": "日付", "attribute_value_mlt": [{"subitem_date_issued_datetime": "2015-07-06", "subitem_date_issued_type": "Created"}]}, "item_20003_date_granted_56": {"attribute_name": "学位授与年月日", "attribute_value_mlt": [{"subitem_dategranted": "2015-02-05"}]}, "item_20003_degree_grantor_58": {"attribute_name": "学位授与機関", "attribute_value_mlt": [{"subitem_degreegrantor": [{"subitem_degreegrantor_name": "松本歯科大学"}], "subitem_degreegrantor_identifier": [{"subitem_degreegrantor_identifier_name": "33602", "subitem_degreegrantor_identifier_scheme": "kakenhi"}]}]}, "item_20003_degree_name_57": {"attribute_name": "学位名", "attribute_value_mlt": [{"subitem_degreename": "博士(歯学)"}]}, "item_20003_description_14": {"attribute_name": "内容記述", "attribute_value_mlt": [{"subitem_description": "補綴装置製作に,生体への親和性からチタンが多用されておりその修復および加工にはレーザ溶接が用いられてる.しかし溶接された領域付近からの再破折 を経験することがある.そうした中,チタン圧延材に一定の条件で熱処理を行うと疲労強度が有意に大きくなるという報告がなされた.本研究は,鋳造,機械加工,MIM(Metal injection molding)の各製作法によるチタン材,およびレーザ溶接後のチタン材に対しても熱処理が有効であるかについて疲労破壊に着目して 検討を行った.試験片は,鋳造 法,機械加工,MIM 法 により,巾2mm,厚さ1mm,長さ30mm の試料を製作して用いた.レーザ溶接は,試験片を低速切断し,切断面を密着させた状態でレーザ溶接した.熱処理は試験片それぞれを450℃の電気炉内にて 40分間大気中で加熱を行った後,炉外にて放冷した.疲労試験は金属曲げ器を用い,ひずみ量0.30mm の反復応力を加え,疲労破折まで回数を測定した.測定は熱 処理を行ったものと未処理のものをそれぞれ5個とした.また,溶接した領域付近の金属組織を観察するため,溶接しした試験片を包埋し,研磨,エッチング後金属顕微鏡にて観察した.またMIM 法 による試験片は,熱処理の有無による気孔率の比較を行った.硬さ試験は組織の観察後の試験片を用い,微少硬度計を用いて荷重100gf,負荷時間10 秒として溶接部周辺のビッカース硬さを測定し,熱処理の有無による違いを分析した.これらの解析により以下示す結果が得れた.1.鋳造によるチタンは,レーザ溶接の有無に かかわらず,熱処理による疲労破壊繰返し数に有意な差は認められかった.3種のチタン材の中で,チタン鋳造体は,疲労破壊に対して最も 弱かった.2.機械加工によるチタンは,レーザ溶接の有無にかかわらず,疲労破壊繰返し数は熱処理により増大した.金属結晶が微細であり,3種のチタン材の中で,疲労破壊に対して最も強かった.3. MIM法によるチタンは,レーザ溶接の有無にかかわらず,疲労破壊繰返し数は熱処理により増大した.また,金属組織中に気孔が観察され,気孔に沿った破折が認められた.", "subitem_description_type": "Other"}, {"subitem_description": "2014", "subitem_description_type": "Other"}]}, "item_20003_description_21": {"attribute_name": "フォーマット", "attribute_value_mlt": [{"subitem_description": "application/pdf", "subitem_description_type": "Other"}]}, "item_20003_description_22": {"attribute_name": "その他の資源識別子", "attribute_value_mlt": [{"subitem_description": "乙第028号", "subitem_description_type": "Other"}]}, "item_20003_dissertation_number_55": {"attribute_name": "学位授与番号", "attribute_value_mlt": [{"subitem_dissertationnumber": "乙第028号"}]}, "item_20003_identifier_23": {"attribute_name": "資源識別子URI", "attribute_value_mlt": [{"subitem_identifier_type": "URI", "subitem_identifier_uri": "http://id.nii.ac.jp/1070/00002405/"}]}, "item_20003_relation_28": {"attribute_name": "情報源", "attribute_value_mlt": [{"subitem_relation_name": [{"subitem_relation_name_text": "http://id.nii.ac.jp/1070/00002421/"}]}]}, "item_20003_relation_30": {"attribute_name": "他の資源との関係", "attribute_value_mlt": [{"subitem_relation_name": [{"subitem_relation_name_text": "投稿雑誌:三溝 恒幸. レーザー溶接したチタン材に対する加熱処理の有効性に関する研究 . 松本歯学. 2015; 41(1): 54-67. © 2016 松本歯科大学学会"}]}]}, "item_20003_text_52": {"attribute_name": "機関ID", "attribute_value_mlt": [{"subitem_text_value": "6"}]}, "item_20003_text_53": {"attribute_name": "コンテンツID", "attribute_value_mlt": [{"subitem_text_value": "oai:mdu.repo.nii.ac.jp:00002417"}]}, "item_20003_text_54": {"attribute_name": "コンテンツ更新日時", "attribute_value_mlt": [{"subitem_text_value": "2022-10-24T06:08:34Z"}]}, "item_20003_version_type_51": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_970fb48d4fbd8a85", "subitem_version_type": "VoR"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "metadata only access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_14cb"}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"download_preview_message": "", "file_order": 0, "filename": "", "future_date_message": "", "is_thumbnail": false, "mimetype": "", "size": 0, "url": {"url": "https://mdu.repo.nii.ac.jp/?action=repository_action_common_download\u0026item_id=2417\u0026item_no=1\u0026attribute_id=20\u0026file_no=1"}, "version_id": ""}, {"download_preview_message": "", "file_order": 1, "filename": "", "future_date_message": "", "is_thumbnail": false, "mimetype": "", "size": 0, "url": {"url": "https://mdu.repo.nii.ac.jp/?action=repository_action_common_download\u0026item_id=2417\u0026item_no=1\u0026attribute_id=20\u0026file_no=2"}, "version_id": ""}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "チタン材", "subitem_subject_scheme": "Other"}, {"subitem_subject": "レーザー溶接", "subitem_subject_scheme": "Other"}, {"subitem_subject": "加熱処理", "subitem_subject_scheme": "Other"}, {"subitem_subject": "疲労強度", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "doctoral thesis", "resourceuri": "http://purl.org/coar/resource_type/c_db06"}]}, "item_title": "レーザー溶接したチタン材に対する加熱処理の有効性に関する研究", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "レーザー溶接したチタン材に対する加熱処理の有効性に関する研究"}]}, "item_type_id": "20003", "owner": "1", "path": ["2589"], "permalink_uri": "https://shinshu.repo.nii.ac.jp/records/23623", "pubdate": {"attribute_name": "公開日", "attribute_value": "2022-11-10"}, "publish_date": "2022-11-10", "publish_status": "0", "recid": "23623", "relation": {}, "relation_version_is_last": true, "title": ["レーザー溶接したチタン材に対する加熱処理の有効性に関する研究"], "weko_shared_id": 1}
レーザー溶接したチタン材に対する加熱処理の有効性に関する研究
https://shinshu.repo.nii.ac.jp/records/23623
https://shinshu.repo.nii.ac.jp/records/23623df7376b5-9dd5-471c-b8da-d4984484c9e0
Item type | Thesis or Dissertation(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2022-11-10 | |||||
タイトル | ||||||
タイトル | レーザー溶接したチタン材に対する加熱処理の有効性に関する研究 | |||||
その他(別言語等)のタイトル | ||||||
その他のタイトル | The influence of heat treatment on the fatigue strength of laser-welded titanium | |||||
作成者(その他言語) |
三溝, 恒幸
× 三溝, 恒幸× Samizo, Tsuneyuki |
|||||
言語 | ||||||
言語 | jpn | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | チタン材 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | レーザー溶接 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 加熱処理 | |||||
キーワード | ||||||
主題Scheme | Other | |||||
主題 | 疲労強度 | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_db06 | |||||
資源タイプ | doctoral thesis | |||||
アクセス権 | ||||||
アクセス権 | metadata only access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_14cb | |||||
内容記述 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 補綴装置製作に,生体への親和性からチタンが多用されておりその修復および加工にはレーザ溶接が用いられてる.しかし溶接された領域付近からの再破折 を経験することがある.そうした中,チタン圧延材に一定の条件で熱処理を行うと疲労強度が有意に大きくなるという報告がなされた.本研究は,鋳造,機械加工,MIM(Metal injection molding)の各製作法によるチタン材,およびレーザ溶接後のチタン材に対しても熱処理が有効であるかについて疲労破壊に着目して 検討を行った.試験片は,鋳造 法,機械加工,MIM 法 により,巾2mm,厚さ1mm,長さ30mm の試料を製作して用いた.レーザ溶接は,試験片を低速切断し,切断面を密着させた状態でレーザ溶接した.熱処理は試験片それぞれを450℃の電気炉内にて 40分間大気中で加熱を行った後,炉外にて放冷した.疲労試験は金属曲げ器を用い,ひずみ量0.30mm の反復応力を加え,疲労破折まで回数を測定した.測定は熱 処理を行ったものと未処理のものをそれぞれ5個とした.また,溶接した領域付近の金属組織を観察するため,溶接しした試験片を包埋し,研磨,エッチング後金属顕微鏡にて観察した.またMIM 法 による試験片は,熱処理の有無による気孔率の比較を行った.硬さ試験は組織の観察後の試験片を用い,微少硬度計を用いて荷重100gf,負荷時間10 秒として溶接部周辺のビッカース硬さを測定し,熱処理の有無による違いを分析した.これらの解析により以下示す結果が得れた.1.鋳造によるチタンは,レーザ溶接の有無に かかわらず,熱処理による疲労破壊繰返し数に有意な差は認められかった.3種のチタン材の中で,チタン鋳造体は,疲労破壊に対して最も 弱かった.2.機械加工によるチタンは,レーザ溶接の有無にかかわらず,疲労破壊繰返し数は熱処理により増大した.金属結晶が微細であり,3種のチタン材の中で,疲労破壊に対して最も強かった.3. MIM法によるチタンは,レーザ溶接の有無にかかわらず,疲労破壊繰返し数は熱処理により増大した.また,金属組織中に気孔が観察され,気孔に沿った破折が認められた. | |||||
内容記述 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 2014 | |||||
日付 | ||||||
日付 | 2015-07-06 | |||||
日付タイプ | Created | |||||
フォーマット | ||||||
内容記述タイプ | Other | |||||
内容記述 | application/pdf | |||||
その他の資源識別子 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 乙第028号 | |||||
資源識別子URI | ||||||
識別子 | http://id.nii.ac.jp/1070/00002405/ | |||||
識別子タイプ | URI | |||||
情報源 | ||||||
関連名称 | http://id.nii.ac.jp/1070/00002421/ | |||||
他の資源との関係 | ||||||
関連名称 | 投稿雑誌:三溝 恒幸. レーザー溶接したチタン材に対する加熱処理の有効性に関する研究 . 松本歯学. 2015; 41(1): 54-67. © 2016 松本歯科大学学会 | |||||
著者版フラグ | ||||||
出版タイプ | VoR | |||||
出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
学位授与番号 | ||||||
学位授与番号 | 乙第028号 | |||||
学位授与年月日 | ||||||
学位授与年月日 | 2015-02-05 | |||||
学位名 | ||||||
学位名 | 博士(歯学) | |||||
学位授与機関 | ||||||
学位授与機関名 | 松本歯科大学 |